Estudio de la elaboración de piedras decorativas a partir de subproductos de la industria alimentaria [semilla de chontilla (Bactris maraja), tagua (Phytelephas macrocarpa), cuesco de palma africana (Elaeis guineensis) y cáscara de coco seco (Cocos nucifera)].
Abstract
Debido a los niveles actuales de contaminación, se plantea como alternativa el
aprovechamiento de subproductos de la Industria agropecuaria para la obtención de
materiales de construcción, para esto y debido a la predisposición y costos ínfimos se
pretende aprovechar subproductos del procesamiento de productos agrícolas, como es el
caso de la semilla de chontilla (bactris maraja), tagua (Phytelephas macrocarpa), cuesco de
palma africana (elaeis guineensis) y cáscara de coco seco (cocos nucifera), esto a fin de
disminuir la huella de carbono, contaminación ambiental (debido a la explotación de los
recursos naturales no renovables). Para la investigación se aplicó un diseño factorial
AxB+1 con tres repeticiones, teniendo como factor A (subproductos agroindustriales), en
el factor B se comprobaron tres tipos de proporciones para la fabricación de las piedras y
como testigo una mezcla estándar utilizada por la empresa Piedra Pacific de Quito-
Ecuador. Se realizó el análisis de la resistencia a la flexión, el porcentaje de absorción de
agua y el peso, estas pruebas se la realizaron en un laboratorio de estudios de suelos y
rocas. El tratamiento que más se acerca al testigo en la resistencia a la flexión es la semilla
de chontilla con una proporción de 20% de cemento, 50% de polvo de arena azul y 30%
del subproducto, en el caso de la absorción de agua el que tuvo un mayor porcentaje fue el
cuesco de palma africana y en el peso la tagua obtuvo un menor valor. Se concluye que el
mejor tratamiento es la semilla de chontilla porque presentó una mayor resistencia, peso
adecuado y con respecto a la absorción de agua no mostró diferencias con los demás
tratamientos por lo que se recomienda utilizar este subproducto debido a que presenta
mejores resultados que el testigo investigado.
Palabras claves:
Resistencia a la flexión, absorción de agua, diseño experimental AxB+1, dosificación.
Description
Due to the current levels of contamination, the use of by-products of the agricultural
industry for obtaining construction materials is considered as an alternative, for this reason
and due to the predisposition and minimum costs, it is intended to take advantage of
byproducts of the processing of agricultural products, as is the case of chontilla seed
(bactris maraja), tagua (Phytelephas macrocarpa), African palm (elaeis guineensis) and dry
coconut shell (cocos nucifera), in order to reduce the carbon footprint, environmental
pollution (due to to the exploitation of non-renewable natural resources). For the research,
a factorial design AxB + 1 with three repetitions was applied, having as factor A (agroindustrial
byproducts), factor B checked three types of proportions for the manufacture of
the stones and as a witness a standard mixture used by the company Pacific Stone of Quito-
Ecuador. The analysis of the resistance to flexion, the percentage of water absorption and
the weight were carried out, these tests were carried out in a soil and rock studies
laboratory. The treatment that comes closest to the control in the resistance to bending is
chontilla seed with a proportion of 20% cement, 50% blue sand powder and 30% byproduct,
in the case of water absorption the that had a higher percentage was the African
palm coconut and in the weight the tagua obtained a lower value. It is concluded that the
best treatment is chontilla seed because it showed greater resistance, adequate weight and
with respect to water absorption showed no differences with the other treatments so it is
recommended to use this byproduct because it has better results than the witness
investigated.
Keywords:
Flexion resistance, water absorption, experimental design AxB + 1, dosage.
Keywords
Resistencia a la flexión, absorción de agua,, diseño experimental AxB+1, dosificación.
Citation
Castro Arias, Kevin Eduardo; Santos Villena, Gabriel Aron. (2018). Estudio de la elaboración de piedras decorativas a partir de subproductos de la industria alimentaria [semilla de chontilla (Bactris maraja), tagua (Phytelephas macrocarpa), cuesco de palma africana (Elaeis guineensis) y cáscara de coco seco (Cocos nucifera)]. Quevedo. UTEQ. 73p.